GMK 2510 Contact Adhesive

GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.
GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.

High Adhesive Strength | Permanently Elastic | Temperature Resistant

GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.

Technical Data
BasePolychloroprene (CR)
ColourBlack
Density0.93 g/cm3
Viscosity1500 mPa·s
Mixing Ratio100 : 7
Pot Life at at 23 °C, 50 % rel. air humidity> 2 hrs
Evaporation Time5 – 15 min
Consumption150 – 300 g/m2
Final Strength (100% strength)24 hrs
Processing Temperature+15 to +35
Shelf Life12 months
Lap Shear strength material thickness. 1.5mm DIN EN 1465
-Galvanized Steel
-Galvanized Steel + EPDM
-Galvanized Steel + SBR
-Galvanized Steel + NBR

3 N/mm2
0.6 N/mm2
0.5 N/mm2
0.49 N/mm2
Temperature Resistance-40 to +80 for a short period of
time (approx. 1 h) to +130 °C
Approval / Guidelines
-IMPA Code
-MIL-Spec comply with

815239/40
MIL-A-21366A

GMK 2510 Contact Adhesive Technical Data Sheet

GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.

GMK 2510 Contact Adhesive Safety Data Sheet

GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.

GMK 2510 Contact Activator Safety Data Sheet

GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather.

GMK 2410 Contact Adhesive Material Packing Sizes

CodeType and Colour
10953001Processing Spatula, 1 PCE
10953003Processing Spatula, 1 PCE
10953020Contour Spatula Flexy, 1 PCE

Adhesive and Sealant in Singapore

FengFu Private Ltd
Email
[email protected]
WhatsApp
+65-8854 6437

Call us at:
+65-9816 1980

FengFu YouTube
FengFu Linkedin
FengFu Facebook

Delivery Locations in Singapore

Locations We Deliver to:
Singapore

We supply GMK 2510Contact Adhesive (GMK 2510 is a 2-component adhesive based on polychloroprene for the full-surface and permanently elastic bonding of parts continuously exposed to dynamic loads. The advantage compared to 1-component contact adhesives is the significantly improved adhesion and higher temperature resistance. GMK 2510 bonds rubber, metal, textiles, leather, sponge rubber (neoprene), CSM (Hypalon), insulating materials, PU materials with an adhesive coating, wood, stones and many plastics. After curing, the joint is resistant to humidity. WEICON GMK 2510 is not suitable for materials such as polystyrene foam, polyethylene, polypropylene parts, PVC soft foam and PVC imitation leather) to Bishan, Braddell, Toa Payoh, Novena, Newton, Orchard, Somerset, Dhoby Ghaut, City Hall, Raffles Place, Marina Bay, Marina South Pier, Pasir Ris, Simei, Tanah Merah, Bedok, Kembangan, Eunos, Paya Lebar, Aljunied, Kallang, Lavender, Bugis, City Hall, Raffles Place, Tanjong Pagar, Outram Park, Tiong Bahru, Redhill, Queenstown, Commonwealth, Buona Vista, Dover, Clementi, Chinese Garden, Lakeside, Boon Lay, Pioneer, Joo Koon, Tuas Crescent, Tuas West Road, Tuas Link, Expo, Changi Airport, HarbourFront, Outram Park, Chinatown, Clarke Quay, Little India, Farrer Park, Boon Keng, Potong Pasir, Woodleigh, Serangoon, Kovan, Hougang, Buangkok, Sengkang, Punggol, Bras Basah, Esplanade, Promenade, Nicoll Highway, Stadium, Mountbatten, Dakota, MacPherson, Tai Seng, Bartley, Lorong Chuan, Marymount, Caldecott, Botanic Gardens, Farrer Road, Holland Village, One-north, Kent Ridge, Haw Par Villa, Pasir Panjang, Labrador Park, Telok Blangah, Bayfront, Bukit Panjang, Cashew, Hillview, Beauty World, King Albert Park, Sixth Avenue, Tan Kah Kee, Stevens, Newton, Rochor, Bugis, Downtown, Telok Ayer, Fort Canning, Bencoolen, Jalan Besar, Bendemeer, Geylang Bahru, Ubi, Bedok North, Tampines West, Tampines, Tampines East, and Upper Changi.